Калыпка куюу, also referred to commonly as shell molding, is comparatively a new casting technique, developed in Germany in the 1940s.
It’s a type of metal casting process that involves pouring molten metal(ferrous or non-ferrous) or alloy into sand and resin which is further heated and shaped to build a mold.
Shell mold casting offers improved surface finish and higher precision compared to other metal casting methods, and suitable for small parts that require complex shapes and high dimensional accuracy.
Shell mold casting is applied to various industries such as aerospace, медициналык, жана автомобиль енер жайлары.
It is especially popular in the automotive industry and is often employed to manufacture camshafts, редукторлор, кранк валдары, цилиндр баштары, bearing housings, lever arms, and valve bodies.
Two matching metal pattern halves—typically machined from steel or iron—are produced to the exact geometry of the desired casting (plus allowances for shrinkage and shell thickness).
Each pattern half is heated (≈180–250 °C), lightly sprayed with a release agent, then dipped into a “dump box” containing fine sand coated in a thermosetting resin.
The hot pattern cures a uniform shell layer (6–12 mm thick) as excess sand is shaken off.
The two cured shell halves are carefully stripped from their patterns.
If internal cavities are required, resin‐bonded sand cores are placed inside one shell half.
The cope (top) and drag (bottom) shells are then clamped together in a flask, and the gating system (карагай, жөө күлүктөр, vents) is attached.
Molten metal or alloy (мис., темир, болот, алюминий) is heated to its liquidus temperature and poured by gravity into the sprue.
The metal fills the shell cavity, replicating fine details and thin sections.
The thin, ceramic‐like shell conducts heat away rapidly.
After an appropriate cooling interval—often just a few minutes at ambient temperature—the metal has solidified into a robust casting.
The flask is opened and the shell fragments are broken away to free the casting.
The part is then freed of any gating or core material and undergoes any required trimming, майдалоо, or surface finishing before inspection.
Shell molding accommodates most ferrous and non-ferrous alloys, мисалы:
| Alloy Family | Typical Grades | Key Properties & Applications |
|---|---|---|
| Gray Iron | ASTM A48 Class 20–40 | Excellent machinability & vibration damping; used for engine blocks, Housings. |
| Уюлдук темир | ASTM A536 60-40-18, 65-45-12 | Higher strength & toughness than gray iron; ideal for gears, кранк валдары, клапандар. |
| Carbon Steel | AISI 1018, 1020, 1045 | Good strength and weldability; used for shafts, кашаалар, структуралык бөлүктөр. |
| Эритме болот | 4140, 4340, H13 | Enhanced hardness, катуулугу, жана туруштук берет; used in dies, аспаптар, оор техника. |
| Дат баспаган болот | 304, 316, 17-4PH, 2205 (Дуплекс) | Corrosion resistance and strength; used in chemical, тамак, медициналык, and marine parts. |
| Алюминий эритмелери | A356, A357, Adc12 | Жеңил, good fluidity; used for automotive brackets, Housings, aerospace fittings. |
| Жез эритмелери | C905 (Тин коло), C836 (Алюминий коло), C230 (Cartridge Brass) | Excellent wear and corrosion resistance; подшипниктерде колдонулат, втулкалар, деңиз аппаратурасы. |
| Nickel-Based Alloys | Inconel 625, Hastelloy C276 | Outstanding high-temperature strength and corrosion resistance; used in aero-engines, химиялык кайра иштетүү. |
| Магний эритмелери | AZ91D, AM60 | Very lightweight; used in electronics housings and automotive components. |
| Zinc Alloys | Zamak 3, Zamak 5 | Low melting point and excellent detail reproduction; used for small, татаал бөлүктөр (hardware, арматуралар). |
1. Proprietary Resin‐Sand Formulations
2. High-Speed, Automated Shell Production
3. Expert Pattern & Tooling Design
4. Broad Alloy Capability
5. Tight Dimensional Control
6. Lean, Green Operations
7. Comprehensive Quality Assurance
8. Dedicated Technical Support
| өнөр жай | Typical Shell Mold Castings | Typical Products |
|---|---|---|
| Автоунаа | Camshaft and crankshaft housings, gearbox and transmission cases, цилиндр баштары, bearing carriers, and linkage arms—benefit from tight tolerances and fine surface finish, reducing or eliminating post-machining. |  |
| Aerospace & Defense | Actuator brackets, fuel-system fittings, small turbine stator segments, control-surface hinges, and structural brackets—leveraging weight-sensitive, high-precision parts where repeatability and fatigue resistance are critical. |  |
| Медициналык аппараттар | Surgical instrument handles and housings, implant-fixture bushings, orthopedic bracketry, and fluid-control valves—requiring complex internal passages, biocompatible alloys, and sterilizable finishes. |  |
| Industrial Valves & Pumps | Precision valve bodies, дөңгөлөктөр, volutes, and pump housings cast in stainless or duplex stainless steels—resisting corrosive media while maintaining exacting dimensional requirements for reliable sealing and flow control. |  |
| Oil & Gas / Нефть-химия | Chemical-service fittings, filter housings, manifold blocks, and instrumentation flanges—taking advantage of exotic alloys (мис., Inconel, Hastelloy) with minimal surface porosity and high dimensional fidelity. |  |
| Consumer & Decorative | Ornamental door handles, lighting fixtures, sculpture components, and architectural accents—shell-cast in brass, коло, or aluminum to capture fine textures and crisp edges. |  |
| Renewable Energy & Power Generation | Small hydraulic turbine nozzles, control-valve bodies, and generator accessory brackets—benefiting from rapid turnaround and the ability to cast heat-resistant alloys with tight wall-thickness control. |  |
| Same side of parting line: | ± .020 for 1st 3″ | Add ± .003 / inch over 3″ |
| Across parting line: | ± .030 for 1st 3″ | ± .003 / inch over 3″ |
| Draft: | Typically 1° | Certain applications at 0° draft. |
| Typical Finish Stock: | .060″ maximum | |
| Hole size cast into part: | DIAMETER | DEPTH |
| Less than 0.5″ | Equal to diameter | |
| 0.5″ – 1.0″ | Equal to 1.5 times diameter | |
| Greater than 1.0″ | Equal to 2 times diameter |
Shell mold casting is a precision sand-based process in which a heated metal pattern is coated with fine, resin-bonded sand to form thin “shell” halves. Once cured and assembled, these shells serve as the mold into which molten metal is poured.
Almost any alloy is suitable—including gray and ductile irons, carbon and alloy steels, дат баспас болоттон жасалган, алюминий эритмелери, copper-based alloys, and even nickel-based superalloys—thanks to the shell’s heat resistance.
Typical dimensional tolerances reach ±0.3 mm per 100 мм, and surface finishes are in the Ra 3–6 µm range. This precision often eliminates or minimizes secondary machining.
Shell molding excels at small to medium components (from a few grams up to about 50 кг). Shell halves larger than this become difficult to handle and may crack under their own weight.
Each shell half cures in roughly 10–30 seconds on automated dip-and-shake equipment. This quick turnaround supports fast prototyping and moderate production volumes.
Intricate details—thin walls (down to 1.5 мм), undercuts, fine ribs, and internal passages—are readily achieved. Cores can be inserted for complex internal cavities.
Select shell molding when your parts require small- to medium-size, Жогорку өлчөмдүү тактык, fine surface quality, and complex detail.
| Критерийлер | Кум куюу | Shell Ford Casting | Инвестициялык кастинг |
|---|---|---|---|
| Форма материалы | Green sand (кремний + clay) | Resin-bonded fine sand shell | Керамикалык кабык (wax patterns dipped in slurry) |
| Курал наркы | Very low | Орто (heated patterns + resin sand) | Жогорку (wax tooling + multiple shell dips) |
| Mold Reuse | Жок (sand broken each pour, but sand is reclaimable) | Жок (each shell single-use, sand reclaimable) | Жок (each ceramic shell single-use) |
| Part Size Range | Very small to very large (> several tons) | Small to medium (up to ~50 kg) | Very small to small (адатта < 10 кг) |
| Өлчөмдүү толеранттуулук | ± 0.5 Мм 100 мм | ± 0.25–0.35 mm per 100 мм | ± 0.15–0.25 mm per 100 мм |
| Беттик бүтүрүү (Ра) | 6–12 µm | 3–6 µm | 1–2 µm |
| Дубалдын калыңдыгы | ≥ 6 мм | ≥ 1.5–2 mm | ≥ 1 мм |
| Татаалдуулук & Detail | Орто (cores required for internal features) | Жогорку (жука дубалдар, fine features easily achieved) | Абдан жогору (undercuts, intricate geometries) |
| Cycle Time | Жай (mold prep, шайкеш) | Тез (shell cures in seconds) | Slowest (multiple coating and dewax steps) |
| Өндүрүштүн көлөмү | Төмөндөн ортого чейин | Төмөндөн ортого чейин | Төмөндөн ортого чейин (100–1,000s parts) |
| Typical Alloys | Темир, болот, алюминий, коло, жана башкалар. | Темир, болот, stainless, алюминий, Жез эритмелери | Stainless, Superarlooys, коло, алюминий |
| Post-processing Needs | Often heavy machining and surface cleanup | Minimal machining; light finishing | Minimal machining; often ready to final shape |
| Best For | Чоң, heavy, cost-sensitive parts | Precision small/medium parts with moderate volume | Extremely intricate, thin-walled, high-accuracy parts |